Acid etching is a technique commonly used in dentistry to prepare a tooth surface for bonding with composite resin materials. It involves the use of an acidic solution, typically phosphoric acid, to remove a thin layer of the tooth's surface, creating a roughened surface that allows for better adhesion of the composite resin.
The acid etching process involves applying the acid solution to the tooth surface for a specific amount of time, typically between 15 and 60 seconds, depending on the manufacturer's recommendations. The acid is then rinsed off with water and the tooth is dried before the composite resin is applied.
The benefits of acid etching include improved bonding strength between the composite resin and tooth structure, as well as reduced microleakage and improved marginal adaptation of the restoration. Acid etching can also help to remove surface stains and discolorations from the tooth.
Exemplos de tradução
Recent orthodontic bonding materials have aimed to reduce the working time of the clinician, by simplifying the acid etching procedure by applying self-etching primer adhesive systems.
Os recentes materiais de colagem dos acessórios ortodônticos têm visado reduzir o tempo de trabalho do clínico, simplificando o procedimento do condicionamento ácido por meio dos sistemas adesivos autocondicionantes.
"Etching" é o processo de remoção da camada superficial de um dado material. Esta remoção pode ser conseguida recorrendo a substâncias químicas que dissolvem ou corroem a superfície do material. O Etching nada mais é do que um processo de corrosão muito bem controlado.
Meaning
Treatment of a surface with an acid, a chemical solution or primer in order to dissolve loose particles or provide a profile. (specialchem4coatings.co...)
Exemplos de tradução
Desorption of the adsorbent may also be obtained by performing acid etching of the latter leading to the destruction of its hydroxylated network consequently causing salting–out of the captured ions.
Também é possível obter a dessorção do adsorvente realizando o ataque ácido do último, levando à destruição de sua rede hidroxilada, causando, como conseqüência, a coagulação dos íons capturados.
Aplicação de ácidos à superfície dos metais para evidenciar sua estrutura granular; feito no condicionamento ácido do esmalte, antes da aplicação dos compósitos.
Exemplos de tradução
Avaliar o efeito de diferentes tempos de condicionamento ácido e
tratamentos de superfície na resistência ao cisalhamento da cerâmica vítrea de
dissilicato de lítio ao cimento resinoso.
To evaluate the effect of different acid etching times and surface
treatments on the shear strength of lithium disilicate vitreous ceramics to resin
cement.
Banco de Glossários (traduções não verificadas)
Área
Inglês
Português
Qualidade
Mecânica
acid etching
ataque químico por ácido
Téc/Geral
acid etching
ataque/condicionamento ácido
Téc/Geral
acid etching
ataque ácido
Mecânica
Black acid etching
ataque ácido preto
Frases traduzidas contendo "acid etching"
Recent orthodontic bonding materials have aimed to reduce the working time of the clinician, by simplifying the acid etching procedure by applying self-etching primer adhesive systems.
Os recentes materiais de colagem dos acessórios ortodônticos têm visado reduzir o tempo de trabalho do clínico, simplificando o procedimento do condicionamento ácido por meio dos sistemas adesivos autocondicionantes.
This in vitro study evaluated the influence of whitening activated with hybrid light on the function variations of the pH level and concentration of bleaching gels and prior acid etching of bovine enamel and the change in roughness and wear after simulated tooth brushing.
Este estudo in vitro avaliou a influência do clareamento ativado com luz híbrida, em função da variação do pH e concentração de géis clareadores, e do condicionamento ácido prévio do esmalte bovino na alteração da rugosidade e desgaste após escovação simulada.
acid etching appear to have a weakening effect on the ceramic surface, if compared to the untreated group.
O condicionamento ácido parece ter um efeito de enfraquecimento sobre a superfície cerâmica, se comparado com o grupo não tratado.
Desorption of the adsorbent may also be obtained by performing acid etching of the latter leading to the destruction of its hydroxylated network consequently causing salting–out of the captured ions.
Também é possível obter a dessorção do adsorvente realizando o ataque ácido do último, levando à destruição de sua rede hidroxilada, causando, como conseqüência, a coagulação dos íons capturados.
The tests were performed in the following experimental sequence: in the presence of smear layer (PMin); after a 15-second acid etching (37% phosphoric acid- PMax); after the application of the desensitizing agents; and after a 1-minute acid challenge (6% citric acid).
Os ensaios foram realizados na seguinte sequência experimental: na presença de smear layer (PMin); após condicionamento com ácido fosfórico a 37%, por 15 segundos (PMax); após a aplicação dos agentes dessensibilizantes e após o desafio com ácido cítrico a 6%, por um minuto.
Purpose: The aim of this study was to compare the biologic and mechanical behavior of bone tissue around implants with commercially available surfaces, modified by acid etching (SA), and machined surfaces (SU), with the experimental surfaces modified by laser (SL), and modified by laser with silica deposition (SS), using biomechanical, topographic and histometric analyses.
Proposição: O objetivo deste estudo foi comparar o comportamento biológico e mecânico do tecido ósseo ao redor de implantes de superfícies comerciais modificada por condicionamento ácido (SA), e usinada (SU), com implantes de superfícies experimentais modificada por laser (SL), e modificada por laser com depósito de sílica (SS), empregando-se as análises biomecânica, topográfica e histométrica.
Desorption of the adsorbent may also be obtained by performing acid etching of the latter leading to the destruction of its hydroxylated network consequently causing salting–out of the captured ions.
Também é possível obter a dessorção do adsorvente realizando o ataque ácido do último, levando à destruição de sua rede hidroxilada, causando, como conseqüência, a coagulação dos íons capturados.
The blocks were cleaned in ultrasonic apparatus with distilled water and dried with compressed air, subjected to acid etching and air-jet washed with water, dried with compressed air and received application of silane agent Monobond-S, followed by adhesive Excite ( Ivoclar Vivaden).
Os blocos foram limpos em aparelho ultrassônico com água destilada e secos com jato de ar, submetidos ao condicionamento ácido e lavados com jatos ar-água, secos com jato de ar e receberam aplicação do agente de silanização Monobond-S, seguido do adesivo Excit (Ivoclar Vivaden).
The introduction of the acid etching technique allowed the development and improvement of the direct fixation of the brackets to the teeth, becoming the direct bonding a routine clinical procedure.
A introdução do condicionamento ácido do esmalte dental permitiu o desenvolvimento e aperfeiçoamento da fixação direta dos acessórios ortodônticos aos dentes, fazendo da colagem direta um procedimento clínico rotineiro.
The lowest values of bond strength were found for the group without previous acid etching with application of 2% chlorhexidine gluconate, but without significant differences for the other groups (p>.05).
Os menores valores de resistência de união foram encontrados para o grupo sem condicionamento ácido prévio e com aplicação de digluconato de clorexidina 2%, mas sem diferença estatística para os demais grupos (p>0,05).
Conclusions: Hydrofluoric acid etching proved to be a treatment capable of altering the surface roughness of Y-TZP and glass, probably, was not able to penetrate the ceramic material and only had the role of protecting the surface from acid etching.
Conclusões: O ataque com ácido fluorídrico demonstrou ser um tratamento capaz de alterar a rugosidade superficial da Y-TZP e o vidro, provavelmente, não foi capaz de penetrar no material cerâmico e teve tão somente o papel de proteger a superfície do ataque ácido.
Sixty feldspathic porcelain disc shaped specimens were randomly divided into 3 groups of 20 each, according to hydrofluoridric acid etching time of either 15, 30 seconds and 1 minute (groups 1, 2 and 3, respectively).
Sessenta espécimes de porcelana em formato cilíndrico foram aleatoriamente divididos em 3 grupos de 20 espécimes de acordo com o tempo de ataque do ácido hidrofluorídrico de 1 minuto, 30 segundos e 15 segundos (grupos 1, 2 e 3 respectivamente).
Only the normal substrate, when rehydrated, after acid etching. with distilled water (control), is the one that presented BS values to the dentin significantly higher to the others.
Apenas o substrato normal, quando reidratado, após condicionamento ácido, com água destilada (controle), é que apresentou valores de RU à dentina significativamente superiores aos demais.
The aim of this double blind split-mouth randomized clinical study was to evaluate, in vivo, the effectiveness of prior acid etching on enamel and low concentration bleaching gels based on hydrogen peroxide (HP) associated with hybrid light (HL) sources, having as response variables: dental sensitivity, dental pulp vascularization and degree of color change and stability over 6 months.
O objetivo deste estudo clínico randomizado duplo cego boca-dividida foi avaliar, in vivo, a efetividade do condicionamento ácido prévio do esmalte e de géis clareadores a base de peróxido de hidrogênio (PH) de baixa concentração, associados a fontes de luz híbrida (LH), tendo como variáveis de reposta: sensibilidade dental, fluxo sanguíneo pulpar, grau de mudança e estabilidade de cor ao longo de 6 meses.
This study evaluated the effect of acid etching of the enamel and the combination of different light sources (halogen light, LED and LED/LASER) with bleaching product on the color change, penetration of hydrogen peroxide and cytotoxicity during the time.
Este estudo avaliou o efeito do condicionamento ácido do esmalte dental e do uso de diferentes fontes luminosas (luz halógena, LED e, LED/LASER) com um produto clareador na alteração de cor, penetração do peróxido de hidrogênio e citotoxicidade ao longo do tempo.
The purpose of this study was to evaluate the effects of low intensity laser in the process of osseointegration of implants with machined surface (SU) and modified by Al2,3 blasting followed by acid etching (SJA), installed in tibias of rabbits using the resonance frequency analysis and removal torque of implants.
A proposição do presente trabalho foi avaliar os efeitos do laser de baixa intensidade no processo de osseointegração de implantes com superfície usinada (SU) e modificada por jateamento de Al2,3 seguido do condicionamento ácido (SJA), instalados em tíbias de coelhos utilizando-se as análises de frequência de ressonância e do torque de remoção dos implantes.
The purpose of this study was to evaluate five hypotheses: a) hydrofluoric acid etching decreases the flexural strength of a feldspathic porcelain; b) cementation increases the flexural strength of a feldspathic porcelain; c) the neutralization process of hydrofluoric acid precipitates decreases the flexural strength of a feldspathic porcelain; d) hydrofluoric acid precipitates cleaning with ultrasonic bath in deionized water, formed on the ceramic surface after acid etching. increases flexural strength values of a feldspathic porcelain; e) the association between the neutralization process of the hydrofluoric acid precipitated and ultrasonic sonic cleaning improves the flexural strength of a feldspathic porcelain.
O objetivo deste trabalho foi avaliar cinco hipóteses: a) o condicionamento ácido diminui a resistência à flexão de uma cerâmica feldspática; b) a cimentação aumenta os valores de resistência à flexão de uma cerâmica feldspática; c) o processo de neutralização dos precipitados do ácido fluorídrico diminui os valores de resistência à flexão de uma cerâmica feldspática; d) a limpeza sônica (ultra-som) com água deionizada dos precipitados do ácido fluorídrico, formados sobre a superfície cerâmica após o condicionamento ácido, aumenta os valores de resistência à flexão de uma cerâmica feldspática; e) a associação entre o processo de neutralização dos precipitados do ácido fluorídrico e a limpeza sônica melhora a resistência à flexão de uma cerâmica feldspática.
The surfaces that mimic acid fractures are created by acid etching specimens in laboratory conditions reduced in scale from those observed in an actual acid fracturing job.
As superfícies que imitam fraturas ácidas são criadas pelo ataque ácido em corpos de prova em condições de laboratório que reproduzem em escala aquelas observadas em um fraturamento ácido real.
The ICL were produced using DE-RE cycling and the specimens were randomized in five groups, according to the treatment (n=12): Vcontrol (5% sodium fluoride varnish during 4h), and four groups previously preatreated with topical application of acidulated phosphate fluoride (APF) during 4min: F (without pretreatment), P-F (phosphoric acid etching during 30s), Al-F (0,05M aluminum nitrate during 1min); P-Al-F (phosphoric acid etching + aluminum nitrate).
LI foram produzidas através de ciclagem Desmineralização-Remineralização (DES-RE) e os espécimes divididos aleatoriamente em cinco grupos, de acordo com o tratamento (n=12): V- controle (verniz de fluoreto de sódio 5% por 4 horas), F (sem pré-tratamento); P-F(condicionamento ácido com ácido fosfórico por 30s); Al-F (nitrato de alumínio a 0,05M por 1min); P-Al-F (condicionamento com ácido fosfórico a 37% + nitrato de alumínio a 0,05M).
The application of the adhesive on the resin composite core, after acid etching. should be avoided.
A aplicação do adesivo dentinário sobre o núcleo de preenchimento, após o condicionamento ácido, deve ser evitada.
For both tests, the following conditions were measured: in the presence of smear layer, after 37% phosphoric acid etching and after the application of the tested materials in the occlusal surfaces of dentin discs.
Para ambos os testes as medidas foram realizadas nas seguintes condições: na presença de smear layer; após condicionamento com ácido fosfórico a 37% e após a aplicação dos materiais na superfície oclusal dos discos de dentina.
The yttria stabilized zirconia (Y- TZP) has excellent mechanical properties, however its inert crystalline microstructure makes treatments applied in porcelain and glass ceramics, such as hydrofluoric acid etching and application of silane compounds, are ineffective for the union resin cements.
A zircônia estabilizada por ítria (Y-TZP) apresenta excelentes propriedades mecânicas; entretanto, sua microestrutura cristalina inerte faz com que tratamentos aplicados em porcelanas e vitrocerâmicas, como condicionamento com ácido fluorídrico e aplicação de compostos silânicos, sejam ineficazes para obter união aos cimentos resinosos.
Thus, the adhesive Adper Single Bond 2 was applied to dentin after 35% phosphoric acid etching for 15 or 7 seconds, and the bond of Clearfil SE Bond after 20 or 10 seconds of primer application.
Desta forma, o adesivo Adper Single Bond 2 foi aplicado à dentina após condicionamento com ácido fosfórico a 35% por 15 ou 7 segundos e o agente de união do Clearfil SE Bond após 20 ou 10 segundos de aplicação do primer.
...uations with little or no enamel structure. When there is a considerable presence of enamel should prio ritize the employment of conventional resin cements or self-adhesive associated with phosphoric acid etching prior to cementation....
...a em esmalte. Quando houver a presença considerável de esmalte deve-se priorizar o emprego dos cimentos resinosos convencionais ou os autoadesivos associados ao condicionamento com ácido fosfórico previamente à cimentação....
.... It were evaluated, clinically, the stability immediate after the surgery and its evolution over the period of eight weeks in implants with the same geometry, diameter and length in two groups: dual acid etching surface (group control) and anodized surface (test group). The groups were evaluated for: insertion torque, initial stability, its evolution in the eight week period and the influence of bone type on...
...ínico, randomizado, controlado, duplo cego e de grupos paralelos. Avaliou-se, clinicamente, a estabilidade no pós-cirúrgico imediato e a sua evolução no período de oito semanas em implantes de mesma macrogeometria, diâmetro e comprimento em dois grupos: implantes de superfície tratada por duplo ataque ácido (grupo controle) e implantes de superfície anodizada (grupo teste). Os grupos foram avaliados quanto ao: torque de inserção, estabilidade inicial pela análise de frequência de ressonância,...
...(yttria-stabilized tetragonal zirconia polycrystal) ceramics have been used to manufacture metal-free tooth- or implantsupported prostheses. However, the conventional surface treatments (hydrofluoric acid etching and silanization) used for silica ceramics are not effective in promoting suitable bonding between resin-based materials and zirconia. Therefore, the purpose of this in vitro study was to evaluate th...
...de ser indicada para restaurações dento ou implantosuportadas. Porém, em função de sua composição, este material apresenta dificuldade de se unir eficazmente com os cimentos, comprometendo assim a longevidade das restaurações. O objetivo desse estudo foi avaliar a influência de diferentes tratamentos de superfície e cimentos na resistência ao cisalhamento (RC) de uma Y-ZTP, assim como a caracterização química da superfície da zircônia após os jateamentos. Duzentos e quarenta discos de Y-ZT...
...he aim of this work, divided in three studies, was to investigate (1) the effect of the substrate, dentin of primary and permanent teeth, as well as, (2) the effect of chlorhexidine application after acid etching on the immediate and (3) long-term bond strength of adhesive systems to dentin. Materials and Methods: In studies 1 and 2, performed in vitro, primary molars and pre-molars were assigned to three gro...
...o: O objetivo deste trabalho, dividido em três estudos, foi (1) investigar o efeito do substrato, dentina de dentes decíduos e permanentes, assim como (2) o efeito imediato e (3) em longo prazo, da aplicação de clorexidina pós-condicionamento ácido da dentina na resistência de união (RU) de sistemas adesivos. Materiais e Métodos: Nos estudos 1 e 2, realizados in vitro, foram utilizados molares decíduos e pré-molares, divididos em três grupos segundo a aplicação dos sistemas adesivos Prime & Bo...
...rmeability after treatments with the desensitizing agents and after acid challenges with different beverages. The dentine permeability was measured after the following sequential steps: (1) after the acid etching of the specimens; (2) after the application of the desensitizing agents; (3) After three sequential acid challenges with different commonly consumed substances (Lemon, vinegar, white wine, coke®, en...
... pressão hidráulica para avaliar as alterações na permeabilidade da dentina após os tratamentos com os agentes dessensibilizantes e após desafios ácidos. A permeabilidade da dentina foi medida após as seguintes etapas sequenciais: (1) após condicionamento ácido dos espécimes; (2) após tratamento com os agentes dessensibilizantes; (3) após três desafios ácidos sequenciais com diferentes substâncias comumente consumidas (limão, vinagre, vinho branco, Coca Cola® e Red Bull®). Os testes de Kr...
...human central incisor. The specimens had been divided trough one longitudinal cut, disdaining the lingual halves The facial halves had received a bicarbonate spurt prophylaxis, ultrasound cleaned and acid etching on the dentin portion. The specimens had been stored in containers contends 25% coffee solution, for two weeks. Finished the period of blackout, initial measurement of the gotten color was carried tr...
...cisivo central humano. Os espécimes foram divididos através de dois cortes longitudinais, desprezando-se as metades linguais. As metades vestibulares receberam profilaxia com jato de bicarbonato, limpeza em ultra-som e condicionamento ácido na porção dentinária. A seguir, os espécimes foram armazenados em recipientes contendo solução de café solúvel a 25%, por duas semanas. Terminado o período de escurecimento, foi realizada mensuração inicial da cor obtida, através do aparelho Easy Shade, qu...
...); specimens without surface treatment had the highest contact angle (65,37˚) whereas HF group exhibited the lowest contact angle (33,80˚). Surface morphological evaluation showed that hydrofluoric acid etching promoted a more obvious surface pattern regarding pores and irregularities with higher surface roughness in comparison to self-etching glass ceramic primer. Finite element analysis showed that lamina...
...fície tiveram o maior ângulo de contato (65, 37˚) entanto que o grupo HF exibiu o menor ângulo de contato (33,80˚). A análise morfológica mostrou que o condicionamento da superfície com HF foi mais obvio mostrando poros, irregularidades e maior rugosidade em comparação com o condicionamento com MEP. A análise por elementos finitos mostrou que o grupo com laminado cerâmico cimentado sobre o esmalte sem preparo apresentou as menores concentrações de tensão tanto no esmalte como no lamina...
...nd presence or absence in pits and fissures. The non-erupted deciduous teeth received priority attention. The scanning electron microscopy was also the methodology elected to study the effects of the acid etching mainly with phosphoric acid under different concentrations, methodologies and application times. It was possible to observe the essential demineralization effects by the acid performance and the vari...
... em fossas e fissuras, predominantemente em dentes decíduos não erupcionados. Foi também analisado pela microscopia eletrônica de varredura os efeitos do condicionamento de diferentes tipos de ácido e, em especial, do ácido fosfórico em diferentes concentrações, metodologias e tempos de aplicação. Estes trabalhos permitiram visualizar as principais ações ácidas desmineralizantes e os tipos de retenções no centro ou periferias dos prismas ou em ambas as regiões, bem como a profundidade e for...
...The aim of this study was to compare the in vivo effectiveness of in-office bleaching technique with hybrid light source (LED and laser therapy), with and without prior acid etching of enamel, depending on the degree of change and stability of color and sensitivity . Upon being informed of the aims of the study was thirty-four volunteers were selected according to the criteria for inclusion and exclusion. Ini...
...este estudo in vivo foi comparar a efetividade da técnica de clareamento em consultório, com fonte de luz híbrida (LED e Laser terapêutico), com e sem condicionamento ácido prévio do esmalte, em função do grau de mudança e estabilidade de cor e sensibilidade. Após serem informados dos objetivos do estudo, trinta e quatro voluntários foram selecionados de acordo com os critérios de inclusão e exclusão. Inicialmente, os voluntários receberam uma profilaxia supra gengival completa, em seguida, f...
...To determine the effect of resin composite placement techniques and the acid etching of the liner on the microleakage of sandwich restorations. Class V cavities were prepared at buccal surface with margins in dentin in sixty bovine incisors. Six groups of ten teeth each were restored as follow: Group A) Single Bond/Z2,0 (2 increments); Group B) Single Bond/Z2,0 (bulk insertion); Group C) Vitrebond with surfac...
...Investigou-se a influência do condicionamento da superfície do cimento de ionômero de vidro modificado por resina e de técnicas de inserção na infiltração marginal de restaurações de resina composta. Foram confeccionadas cavidades classe V (profundidade de 1,5 mm e largura/altura de 3,0 mm) em 60 dentes bovinos, com margens totalmente em dentina coronária após lixamento do esmalte. Os dentes foram divididos em seis grupos e restaurados: Grupo A: Single Bond/Z2,0 (2 incrementos); Grupo B: Single ...
...kayama, Japão), and the teeth of group III, prior to application of the self-etching adhesive system Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão), received the phosphoric acid etching only in enamel. All teeth were restored with composite resin Amelogen Plus (Ultradent Products, Inc., South Jordan, USA). Two calibrated examiners performed the clinical and clinical/digital analysis...
...aplicação do sistema adesivo autocondicionante Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão); os do grupo III, previamente à aplicação do sistema adesivo autocondicionante Clearfil Protect Bond (Kuraray Medical Inc., Kurashiki, Okayama, Japão), receberam o condicionamento com ácido fosfórico apenas em esmalte. Todos os dentes foram restaurados com a resina composta Amelogen Plus (Ultradent Products, Inc., South Jordan, USA). Após o acabamento e polimento, bem como aos 12 ...
...e performance of two adhesive systems in bonding failures over a 10-month period. TransbondTM Plus Self etching primer (3M Unitek, Monrovia, Calif) was compared to conventional bonding technique with acid etching and priming (TransbondTM XT primer, 3M Unitek, Monrovia, Calif.) using split-mouth technique in seventy two teeth, in three patients. A replication technique was used to compare the remaining resin a...
...co de dois sistemas de colagem direta de acessórios ortodônticos por um período de dez meses. A comparação foi feita colando-se os hemi-arcos direitos com o sistema Transbond™ Plus Self-etching primer (SEP) e os hemi-arcos esquerdos com o sistema convencional de condicionamento com ácido fosfórico 37% e aplicação de primer Transbond™ XT. Réplicas em resina epóxica da superfície vestibular dos dentes foram obtidas para avaliar a área de resina remanescente em cada um dos sistemas ades...
...eatments were performed in the following way: Group 2 - new increment was inserted and polymerized directly on the contaminated surface; Group 3 - contaminated surface was treated with 35% phosphoric acid etching and adhesive was applied prior to the insertion of the new increment; Group 4 - diamond bur roughening, 35% phosphoric acid etching. adhesive application and insertion of the new composite increment....
... da seguinte forma: Grupo 2 - resina composta inserida e polimerizada sobre a superfície contaminada; Grupo 3 - condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta; Grupo 4 - asperização com ponta diamantada, condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta. Após a confecção, os espécimes foram armazenados em água a 37oC durante 24h, sendo em seguida montados em uma máquina universal de ensaios para r...
...Variance and Tukey s test (5%). Results: Means (MPa) were: ARCe: 50,5; U1,0e: 24,5; a+U1,0e: 53,5; ARCd: 36,0; U1,0d: 26,7; a+U1,0d: 25,9. No statistical difference was found between groups that used acid etching in enamel, thus presenting values higher than U1,0 without previous acid etching. In dentin, values were higher (p<0,05) for ARCd compared to U1,0d and a+U1,0d groups, which presented similar results...
...s: As médias (MPa) foram: ARCe: 50,5; U1,0e: 24,5; a+U1,0e: 53,5; ARCd: 36,0; U1,0d: 26,7; a+U1,0d: 25,9. Não houve diferença estatística entre os grupos que utilizaram condicionamento ácido em esmalte, sendo superiores ao U1,0 sem condicionamento ácido prévio. Em dentina, os valores apresentaram-se maiores (p<0,05) no grupo ARCd que nos grupos U1,0d e a+U1,0d, sendo que esses últimos apresentaram resultados similares. Conclusões: O condicionamento ácido prévio à cimentação em esmalte melhorou...
...The aim of this study was to evaluate the effect of hard machining, thermal cycle for glazing and acid etching on the surface roughness and flexural strength of a leucite glass-ceramic. Additionally, it was investigated whether the roughness after machining would be influenced by the machining order and by the pair of burs employed. Six pair of burs were used to produce 1,4 discs by automated machining, which...
...O presente trabalho objetivou avaliar o efeito da usinagem de corte duro, do ciclo térmico de glazeamento e do condicionamento ácido na rugosidade superficial e na resistência flexural de uma cerâmica vítrea reforçada por leucita. Adicionalmente, buscou-se investigar se a rugosidade após usinagem seria influenciada pela ordem de usinagem e pelo par de brocas utilizado. Seis pares de brocas foram empregados na confecção de 1,4 discos por usinagem automatizada, os quais foram divididos nos grupos (n=...
...9,1) showed higher bond strengths than OS (33,6 ± 11,6). The mean bond strength for IM-group (42,5 ± 8,7) was statistically superior to 12M (33,3 ± 11,8). The use of 10% sodium hypochlorite, after acid etching. did not improve the immediate and the long term resin-dentin bond strengths for acetone and water/alcohol based adhesive systems....
...05). Somente os fatores principais Adesivo e Tempo de armazenagem foram significantes (p = 0,04 e p = 0,03, respectivamente). O adesivo SB (43,3 ± 9,1 MPa) apresentou altos valores de resistência de união quando comparado com o OS (33,3 ± 11,6 MPa). A resistência de união do grupo IM (42,5 ± 8,7) foi estatisticamente superior à grupo 12M (33,3 ± 11,8)....
...osphoric acid or recived a self-etching aplication, before pit and fissures sealing. Just 6 study groups was formed with 6 especimens each one; the especimens of Goups I, III and V recived phocphoric acid etching aplication (35%), during 30 seconds and the especimens of Groups II, IV and VI recived the Adper Prompt L Pop self-etching aplication, before occlusal sealing with Climpro (Gourps I and II), Vitrosea...
...sivo autocondicionante, previamente a realização do selamento das fóssulas e fissuras. Foram formados 6 grupos de estudo com 6 espécimes cada; os dos Grupos I, III e V receberam a aplicação do condicionamento com ácido fosfórico a 35%, pelo tempo de 30 segundos e os dos grupos II, IV e VI a aplicação do adesivo autocondicionante Adper Prompt L Pop, previamente a realização do selamento oclusal com os materiais Climpro (Grupos I e II), Vitroseal (Grupos IIII e IV), e Fugi II (Grupos V e VI). Apó...
...cated from wax ups of resin and wax and were cast with chromium cobalt alloy. The composite resin used was one of the last generation, monomodal type, photopolymerized and binded to the enamel by the acid etching technique. Tests were carried out in aqueous enviroment. Is was established a maximum of 5,000 cycles for each of the samples. Observatins were made from 1,0 to 1,0 cycles until 2,000 and from 2,0 to...
...s foram obtidos a partir de esculturas com resina acrílica e cera e fundidos em liga de cobalto cromo. A resina composta usada foi de última geração, do tipo monomodal, fotopolimerizável e retida no esmalte através de ataque ácido. Os testes foram realizados em meio aquoso, estabelecendo-se para cada corpo de prova cinco mil ciclos. Foram feitas verificações a cada cem ciclos até dois mil e a cada duzentos ciclos até o total de cinco mil. Os resultados mostraram que as variações na quantidade d...
...High-strength alumina based ceramic crowns are widely used in dentistry due to their favorable esthetic, however, the large amount of crystalline contents jeopardizes their acid etching property and the ideal luting remains unclear. Procera AllCeram restorations exhibits on their intaglio surface micro irregularities optimizing the bonding to resin, with no need for additional conditioning procedures. Purpose...
...Coroas cerâmicas apoiadas sobre infra-estruturas de alumina densamente sinterizada configuram-se como excelentes opções para a reabilitação protética em casos de exigência estética, contudo, o aumento do conteúdo cristalino inviabiliza seu condicionamento por ácidos deixando a maneira ideal de cimentá-las ainda desconhecida. Coroas Procera AllCeram apresentam, em sua face interna, micro irregularidades interessantes ao embricamento e adesão resinosa, dispensando manobras de condicionamento. Obje...
...ental substrate features, the Er:YAG laser (2,94 mm) technology plays a role as an efficient tool in dentin surface treatment, performed in low energy density, whether isolated or in association with acid etching. In order to obtain a more uniform mircro-retentive zone (hybrid layer, tags and microtags) and to avoid the critical aspects on adhesion such as the collagenous demineralized zone collapse, it has b...
...ntal, a tecnologia a laser de Er:YAG (2,94 mm) apresenta-se como recurso eficiente para o tratamento superficial da dentina, isoladamente ou em associação ao condicionamento ácido, em baixa densidade de energia. Para obtenção de uma zona microrretentiva (camada híbrida, tags e microtags) mais uniforme e evitarem-se aspectos críticos de adesão como o colapso da trama protéica, sua remoção pela desproteinização com hipoclorito de sódio (NaOCl) tem sido proposta. O presente estudo teve por objeti...
...The conventional surface treatment performed on feldspathic ceramic is the fluoridric acid etching and silane application. But in several studies the etching has been questioned for its chemical toxicity. Thus this study aimed to evaluate the effect of heat treatment on silanized feldspathic ceramic bond strength to resin cement. Through an in vitro study 24 feldspathic ceramic sintered blocks were sectioned;...
...Os tratamentos de superfície convencionais realizados em cerâmicas feldspáticas são o condicionamento com ácido fluorídrico e a aplicação do silano. Porém em inúmeros estudos o condicionamento ácido tem sido questionado por sua toxidade química. Assim objetivou-se avaliar o efeito do tratamento térmico na cerâmica feldspática silanizada na adesão ao cimento resinoso. Por meio de um estudo in vitro foram seccionados 24 blocos de cerâmica feldspática sinterizada, com dimensões de 5 x 10 x 4...
...ive systems. These adhesives enable the clinician to select the most appropriate protocol for each clinical situation, allowing its application in different adhesion strategies, with or without prior acid etching. In daily practice, professionals commonly deal with substrates in different conditions from which the materials were originally developed. Considering that adhesion to enamel plays an important role...
...sua aplicação sob diferentes estratégias, com ou sem condicionamento prévio com ácido fosfórico. Na prática diária, os profissionais comumente se deparam com substratos em condições diferentes das quais os materiais foram originalmente desenvolvidos. Considerando que a adesão ao esmalte desempenha papel importante na longevidade da união resina/dentina, a presença de esmalte com perda mineral nas margens de preparos conservadores pode comprometer as restaurações. O desempenho dos adesivos uni...
...tion. Ceramic-cement interface was either bonded or not; cement-dentin was always bonded. Stress data were used for load-to-fracture predictions, using literature strengths accounting for milling and acid etching. Mark II® (Vita Zahnfabrik) crowns were milled (Cerec InLab®, Sirona), etched and cemented (Multilink Automix®, Ivoclar) to dentin analogs (NEMA G-10) (n=6). Non-bonding was achieved by applying a...
...a carga de 5,0 N foi aplicada com um pistão de extremidade circular plana (2 mm de diâmetro) sobre as coroas. A contração de polimerização do cimento foi simulada através de contração térmica. O contato entre cimento e cerâmica foi configurado para “união” e “ausência de união”. O contato cimento-troquel foi sempre do tipo “união”. As tensões dadas pela AEF foram utilizadas para o cálculo de cargas para fratura, levando-se em conta os efeitos deletérios da usinagem e do condici...
...oup was immediately measured in micro-Raman spectroscopy. Data were statistically analyzed by ANOVA two criteria and multiple comparisons Tukey test (p <0,05). The deproteinization of dentine without acid etching increased the RU values of the two cements in immediate groups. The dentine deproteinization decreased the GC for both cements. After the mechanical cycling, this technique was effective for ME...
...icro-Raman. Os dados foram estatisticamente analisados por Análise de Variância a dois critérios e teste de comparações múltiplas de Tukey (p<0,05). A desproteinização da dentina sem condicionamento ácido prévio aumentou os valores de RU dos dois cimentos nos grupos imediatos. A desproteinização dentinária diminuiu o GC para os dois cimentos. Após a ciclagem mecânica, essa técnica foi efetiva para o ME, mas não afetou a resistência de união do RU. Os grupos experimentais apresentar...
...otocol in dentin impregnated with different endodontic sealers using 95% ethanol (E) or xylol (X) and its effects on adhesive interface and on bond strength of etch-and-rinse adhesive system when the acid etching (AE) was immediately (I) carried out or 7 days delay (D).Publication 1:Fifty bovine incisors specimens were impregnated with epoxy resin-based sealer (AH Plus) sealer and divided into four groups (n ...
...a por AH Plus e MTA Fillapex, proporcionada pelo etanol a 95,0% (E) ou xilol (X) e seus efeitos sobre a interface adesiva e resistência de união do sistema adesivo etch-and-rinse, com condicionamento ácido (CA) imediato (I) ou após 7 dias (T). Publicação 1: Cinquenta espécimes de coroas de incisivos bovinos foram impregnados com o cimento e divididos em quatro grupos (n=10): G1(EICA), E e CA imediato; G2(XICA), X e CA imediato; G3(ETCA), E e CA após 7 dias e G4(XTCA), X e CA após 7 dias e G5(contro...
...The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose o...
...As desvantagens geradas pela técnica do condicionamento ácido total como o aumento da permeabilidade e umidade superficial, do potencial de denaturação do colágeno, a criação da zona de fragilidade e a citotoxicidade dos monômeros adesivos, sobretudo em função da profundidade, têm estimulado a pesquisa de novos tratamentos do substrato dentinário. Este trabalho tem como objetivo avaliar os efeitos do pré-tratamento da dentina com irradiação laser, condicionamento ácido e hipermineralização...
...er scanning electron microscopy (SEM). Interfaces of two untested beams were also observed under SEM. Moreover, the dentin surface of one additional tooth received SB application (with neither acid etching nor laser irradiation), a composite crown was built-up on it and the tooth was cut longitudinally in two halves, which had their dentin/resin interfaces observed under SEM. This study showed t...
...ob tração. Espécimes fraturados, representativos dos diferentes grupos, tiveram suas superfícies dentinárias observadas ao microscópio eletrônico de varredura (MEV). As interfaces adesivas de 2 espécimes não testados em cada grupo também foram observadas ao MEV. O sistema SB foi aplicado na superfície do dente remanescente (sem ácido e sem laser), a coroa de resina construída e o conjunto seccionado em duas metades, para observação da interface ao MEV. Os resultados mostraram qu...
...HX) application on resin-dentin bond strength in teeth restored with conventional adhesive. The study sample consisted of 30 human third molars, of which the dentin was exposed followed by phosphoric acid etching. The specimens were distributed in three main groups (CHX, thermal denaturation and control). Thermal denaturation consisted of immersion in water at 50ºC for 10 minutes. Control and thermal denatur...
...os 30 terceiros molares humanos que tiveram a dentina superficial exposta, seguido do condicionamento com ácido fosfórico e divididos em três grupos. O grupo controle e grupo CHX foram imersos em água a 37ºC durante 10 minutos e o grupo desnaturação em água a 50ºC durante 10 minutos. O grupo controle e desnaturação foram tratados de acordo com as instruções dos fabricantes e o grupo CHX com clorexidina a 2% após o condicionamento ácido e antes da aplicação do sistema adesivo. Os espécimes ...