With the objective of evaluate how the heat-input and the welding speed influence the HF-ERW process it is proposed to combine these parameters during the production of 13,3/8” outside diameter, 0,380” wall thickness, API 5L standard, X56 steel grade, pipes.
A fim de se avaliar como o aporte de calor e a velocidade de soldagem influenciam na tenacidade da junta soldada pelo processo HF-ERW, é proposto a realização de combinações entre esses parâmetros durante a produção de tubos de 13,3/8” de diâmetro externo, 0,380” de espessura da parede, norma de fabricação API 5L, grau do aço X56.
...btained in the laboratory, the DOE (Design Of Experiments). The main parameters found were the soak temperature, strip speed or time of material in the soak temperature, material thickness and steel grade. In conclusion, the temperature was the most important variable found. An ideal temperature range is presented, in which this steel has the yield strength, according to costumer specifications....
...zado o DOE (Design Of Experments). Os principais parâmetros encontrados foram a temperatura de encharque, velocidade da tira ou tempo do material na temperatura de encharque, espessura do material e grau do aço. Conclui-se ao fim do trabalho, que a temperatura é a variável mais importante. É apresentada uma faixa de temperatura ideal, na qual, este aço apresenta o limite de escoamento, de acordo com as especificações do cliente....
Inglês
Português
Resultados da busca para 