Aqueous solutions of complex salts from these copolymers and surfactants were characterized by light scattering and small angle X-rays scattering techniques.
A mistura estequiométrica desses sais complexos forma dispersões coloidais de agregados com estrutura núcleo-casca. cuja estabilidade cinética depende do tamanho do bloco neutro do copolímero.
...rgest nonlinear coefficients and wide transparency window (up to 5μm). The core-cladding preforms was produced by sucking method and systematically characterized about the core uniformity and concentricity, and also the interface quality by Tm3+ Raman fluorescence containing in the core. It been produced a multimode step index optical fiber with an attenuation of 11,9 dB/m at 6,3 nm. Were also produced microstructured ...
...se de TeO2) apresentaram os maiores coeficientes ópticos não lineares e larga janela de transparência (até 5 μm), o que motivou a produção de fibras ópticas desses materiais. As preformas com estrutura núcleo-casca foram produzidas pelo método de sucção e sistematicamente caracterizadas quanto à uniformidade e centricidade do núcleo e quanto a qualidade da interface, utilizando fluorescência Raman de íons Tm3+ no núcleo. Foram produzidas fibras ópticas de índice degrau multimodo, com atenuação de ...